Soft Magnetic Alloy 1J79

Hangzhou Ualloy Material Co.,Ltd is one of the best soft magnetic alloy 1j79 manufacturers and suppliers in China,Website:http://www.alloystrip.com, welcome to buy discount and low price ni79mo4, e11c, malloy, permalloy 1j79, 79hm from us, and also welcome to check the price and quotation with our factory. Soft magnetic alloy-1J79 (Common Name: Ni79Mo4, E11c, malloy, permalloy, 79HM) 1J79 is a nickel–iron magnetic alloy, with about 80% nickel and 20% iron content. Invented in 1914 by physicist Gustav Elmen at Bell Telephone Laboratories, it is notable for its very high magnetic permeability, which makes it useful as a magnetic core material in electrical and electronic equipment, and also in magnetic shielding to block magnetic fields. Commercial permalloy alloys typically have relative permeability of around 100,000, compared to several thousand for ordinary steel. In addition to high permeability, its other magnetic properties are low coercivity, near zero magnetostriction, and significant anisotropic magnetoresistance. The low magnetostriction is critical for industrial applications, allowing it to be used in thin films where variable stresses would otherwise cause a ruinously large variation in magnetic properties. Permalloy's electrical resistivity can vary as much as 5% depending on the strength and the direction of an applied magnetic field. Permalloys typically have the face centered cubic crystal structure with a lattice constant of approximately 0.355 nm in the vicinity of a nickel concentration of 80%. A disadvantage of permalloy is that it is not very ductile or workable, so applications requiring elaborate shapes, such as magnetic shields, are made of other high permeability alloys such as mu metal. Permalloy is used in transformer laminations and magnetic recording heads. 1J79 widely used in radio-electronic industry, precision instruments, remote control and automatic control system. Normal composition% Ni 78.5~80.0 Fe Bal. Mn 0.6~1.1 Si 0.3~0.5 Mo 3.8~4.1 Cu ≤0.2 C ≤0.03 P ≤0.02 S ≤0.02 Typical Mechanical properties Yield strength Tensile Strength Elongation Mpa Mpa % 980 1030 3~50 Typical Physical properties Density (g/cm3) 8.6 Electrical resistivity at 20℃(Ωmm2/m) 0.55 Coefficient of linear expansion（20℃~200℃）X10-6/℃ 10.3~11.5 Saturation magnetostriction coefficient λθ/ 10-6 2.0 Curie point   Tc/ ℃ 450 The magnetic properties of alloys with high permeability in weak fields 1J79 Initial permeability Maximum permeability Coercivity Saturation magnetic induction intensity Сold-rolled strip/ sheet. Thickness, mm μ0.08/ (mH/m) μm/ (mH/m) Hc/ (A/m) BS/ T ≥ ≤ 0.01 mm 17.5 87.5 5.6 0.75 0.1~0.19 mm 25.0 162.5 2.4 0.2~0.34 mm 28.0 225.0 1.6 0.35~1.0 mm 30.0 250.0 1.6 1.1~2.5 mm 27.5 225.0 1.6 2.6~3.0 mm 26.3 187.5 2.0 cold drawn wire 0.1 mm 6.3 50 6.4 Bar 8-100 mm 25 100 3.2 Mode of heat treatment  1J79 Annealing media Vacuum with a residual pressure not higher than 0.1Pa, hydrogen with a dew point of not higher than minus 40 ℃. The heating temperature and rate 1100~1150℃ Holding time 3~6 Cooling rate With 100 ~ 200 ℃/ h cooled to 600 ℃, rapidly cooled to 300℃ Style of supply Alloys Name Type Dimension 1J79 Wire D= 0.1~8mm -1J79 Strip W= 8~390mm T= 0.3mm 1J79 Foil W= 10~100mm T= 0.01~0.1 1J79 Bar Dia= 8~100mm L= 50~1000