Click image to view original image
Sintered metal filter is made by pressing and sintering metal powder. Its purpose is to generate strong enough material base to ensure mechanical strength of the component and also a porous structure acting as a filter. The advantage of this structure is that unique shapes can be formed by molding instead of costly machining operations.
Product Characteristics
1.Particle size distribution is uniform and narrow, passing rate is more accurate.
2. Low density and high purity
3. Low oxygen level
High Temperature Alloy Powder
1. Particle size distribution is uniform and narrow, passing rate is more accurate.
2.Using effective way to successfully reduce the apparent density of high temperature alloy powder and make pressing no longer difficult.
3.Low oxygen level
Stainless Steel Powder for Porous components
|
Product Characteristics |
|||||||||
|
1.Particle size distribution is uniform and narrow, passing rate is more accurate. |
|||||||||
|
Chemical Compositions |
|||||||||
| C | Si | Mn | Ni | Cr | S | P | Mo | Fe | |
| 316L | ≤0.02 | ≤1.00 | ≤2.00 | 12.0-15.0 | 16.0-18.0 | ≤0.02 | ≤0.02 | 2.0-3.0 | Bal. |
| 304L | ≤0.03 | ≤1.00 | ≤2.00 | 9.0～13.0 | 18.0-20.0 | ≤0.02 | ≤0.02 | - | Bal. |
| 310S | ≤0.02 | ≤0.5 | ≤2.00 | 19.0-22.0 | 24.0-26.0 | ≤0.02 | ≤0.02 | - | Bal. |
High Temperature Alloy Powder| Product Characteristics | |||||||||||
| 1. Particle size distribution is uniform and narrow, passing rate is more accurate. 2.Using effective way to successfully reduce the apparent density of high temperature alloy powder and make pressing no longer difficult. 3.Low oxygen level |
|||||||||||
| Chemical Compositions | |||||||||||
| C | Si | Mn | Ni | Cu | Cr | Fe | Mo | W | Co | V | |
| Monel 400 | ≤0.02 | ≤1.00 | ≤1.00 | 63-69 | 28-34 | - | ≤2.5 | - | - | - | - |
| HastelloyC-22 | ≤0.08 | ≤1.00 | ≤1.00 | Bal | - | 20-22 | 2-6 | 12.5-14.5 | 2.5-3.5 | ≤2.5 | ≤0.35 |
| Inconel 600 | ≤0.03 | ≤0.5 | ≤1.00 | 72-78 | ≤0.5 | 14-17 | 6-10 | - | - | - | - |