Non Toxic Odorless Bopp Thermal Lamination Film Environmentally Friendly

 

Non Toxic Odorless Bopp Thermal Lamination Film Environmentally Friendly

 

 

Glossy Specifications:

 

TYPE	THICKNESS (micron)
GLOSSY	TOTAL	BASE	EVA
	17	12	5
	18	12	6
	20	12	8
	22	12	10
	23	15	8
	25	15	10
	27	15	12
	30	15	15
	42	28	14
WIDTH (mm)	200 ~ 2210
LENGTH (m)	100 ~ 8000
PAPER CORE	25.4mm(1 inch) / 76mm (3 inch)
BONDING	≤2
CORONA TREATED	Double side
SURFACE TENSION	38 Dyne/cm ≤ 42 Dyne/cm
LAMINATION TEMP.	90±10°C
ROLLER PRESSURE	10 ~ 20Mpa
LAMINATION SPEED	20 ~ 70M

 

 

Matte Specifications:

 

TYPE	THICKNESS (micron)
MATTE	TOTAL	BASE	EVA
	17	12	5
	18	12	6
	20	12	8
	22	12	10
	23	15	8
	25	15	10
	27	15	12
	30	15	15
	43	28	15
WIDTH (mm)	200 ~ 2210
LENGTH (m)	100 ~ 8000
PAPER CORE	25.4mm(1 inch) / 76mm (3 inch)
BONDING	≤2
CORONA TREATED	Double side
SURFACE TENSION	38 Dyne/cm ≤ 42 Dyne/cm
LAMINATION TEMP.	90±10°C
ROLLER PRESSURE	10 ~ 20Mpa
LAMINATION SPEED	20 ~ 70M

 

 

Description:

 

Thermal Lamination Films have extrusion-coated surface with low temperature melting resin, which enables the lamination of film to paper products by heat and pressure. Various surface finishes available add value to the printed surface.

 

Glossy BOPP thermal lamination film offers a shiny colorful finish. Its use can enhance the look and increase all laminated presswork’s useful lifetime. Matt BOPP thermal lamination film provides a matt-finish on the surface of presswork, protecting from fingerprints and smudges. Compared with gloss thermal lamination film, matt film can be preserved for longer period of time.

 

23 Micron BOPP thermal lamination film ( so called hot laminating film, dry lamination film ) is widely used for lamination in all kinds of printed & unprinted paper and paper boards, including book covers, cosmetics packaging, magazines, documents, shopping bags, Diaries etc.

 

---

 

The advantages of NEI BOPP thermal lamination film

 

1. Environmentally friendly: It is non-toxic, odorless, or non-benzene because non-solvent based adhesive is used. It is environmentally friendly and non-hazardous to human health since no toxic gases or volatile content is emitted during lamination process. In addition, it is easier to recycle than water-based lamination film because film and paper can be easily separated.

2. Safe operation

3. Excellent performance: Compared with wet lamination, thermal lamination film enhances the color saturation and brightness of presswork. It also has stronger ability of absorbing powder and adhesive force. Furthermore, it is effective to prevent being blistered or separated from presswork in lamination process. As it has strong adhesive ability and surface tension, it can be used for latter processes, including spot UV, hot stamping, die cutting, indentation process.

4. Easy handling

 

5. High efficiency: Production cost and labor cost are reduced substantially as there is no film wastage, mixture of adhesive solvent, or no UV heating lamp (drying system) is required. Therefore, it saves production space as well.

6. Wide adaptability: It is widely adaptable to different types of lamination machines, including wet and dry laminator. Only small adjustments need to be made to the machine if wet laminator is used.

 

---

 

The Brand --- NEI

 

1. NEI has professional experience in film industry since 1995 so we have good quality control and after-sale services to support you.

 

2. 10 yeas of export experience to many countries, including South America, North America, Middle East, Asia, Africa, Oceania, etc. so we have good reputation in these areas.

 

3. Compared with other thermal lamination film, our EVA glue is 100% imported from Korea and it ensures the adhesiveness of our film.

 

4. Customize size and thickness according to customer requests. Labels can be customized as well.

 

5. Rapid production and delivery.

 

6. A wide range of thermal lamination film and special films.

 

---

 

Special Instruction:

 

1. NEI BOPP thermal lamination film is suggested to be laminated with the roller temperature range of 85 to 110°C and roller pressure of 10 to 20 Mpa. However, the optimum conditions are depending on the selected laminator’s speed and dimensional stability.

 

2. It is advised that the printed surface is well dried before lamination and cools sufficiently one surface before laminating to other surface.