Size: 3，6, 8，9, 10,13,16,19,25,30,32,38,50,65,70,75,100
|
Chemical composition |
Al2O3(%) |
92 |
95 |
99 |
|
|
Fe2O3(%) |
≤0.4 |
≤0.3 |
≤0.1 |
|
|
The remaining ingredients can be determined by negotiation between the supplier and the buyer as necessary. |
|||
|
Water absorptivity (%) |
3±1.Can also be negotiated
|
|||
|
Proportion（kg/m³） |
≥3.1 |
≥3.2 |
≥3.4 |
|
|
Bulk density（kg/m³） |
1700-1950 |
1800-1950 |
≥1900 |
|
|
Dust, cracking or breaking |
Single bag less than 5%
|
|||
|
Size deviation
|
Uniform sphere, the ratio of the maximum and minimum diameter of a porcelain ball does not exceed 1.2
|
|||
|
Load softening（yb/t370-1995） |
Less than 0.6% deformation under 0.2 Mpa |
|||
|
Thermal shock resistance (yb/t376.2-1995） |
1200℃ reduced to 600℃, 10 times no cracks on the surface |
|||
|
Reheating heat change (gb/t3997.1-1998) |
1400℃ for 12 hours with a maximum of 0.25% and an average of less tahn 0.20% |
|||