refractory grade WFA white aluminum oxide granular 6-14mesh

refractory grade WFA white aluminum oxide granular 6-14mesh  Description:

refractory grade WFA white aluminum oxide granular 6-14mesh  (White corundum), was made from the high quality alumina by melting above 2000 in the electric arc furnace and cooling. It is white with the main crystal phase alpha-Al2O3. White corundum is a high-level refarctroy raw material with Al2O3 purity up to 99%.It can work as refractory castable, aggregate,refractory coating etc.

refractory grade WFA white aluminum oxide granular 6-14mesh  Characteristic:

With smelting point up to 2250℃, white aluminum oxide is a high level refractory material. It has advantages including high purity,good acid-alkali resistance, temperature resistance, high thermal stability.

refractory grade WFA white aluminum oxide granular 6-14mesh  Applications:

Refractory castable and aggregate.

Kiln construction.

Furnace building.

Refractory coating paint.

Coating sand for Precision casting and 3D printing.

Ceramic Tiles special ceramics.

Technical ceramics.

TYPICAL CHEMICAL ANALYSIS
Section Sand	AL2O3	≥99.5%
	Fe2O3	≤0.08%
	NA2O	≤0.30%
Fine powder	AL2O3	≥99%
	Fe2O3	≤0.25%
	NA2O	≤0.40%
TYPICAL PHYSICAL PROPERTIES
Hardness:	Mohs:9.0
Maximum service temperature:	1900 ℃
Melting Point:	2250 ℃
Specific Gravity:	3.95g/cm3
Volume denstiy	3.6g/cm3
Bulk density(LPD):	1.55-1.95 g/cm3
Color:	White
Particle shape:	Angular
AVAILABLE SIZES
Section Sand	0-1mm,1-3mm,3-5mm,5-8mm
Fine powder	200#-0 320#-0