Linear low density polyethylene(LLDPE)
CAS No.: 9002-88-4
Type: Synthetic Resin and Plastics
Appearance: Transparent beads
Linear low density polyethylene(LLDPE)
Color: Transparent
Density: 0.915-0.940
Property:
1. With high transparency, no discoloration, good self-adhesive, good retraction ratio, good tensile properties, 1 meter can be on 3-5 meters use.
2. Non-toxic, tear-resistant, anti-puncture, hot temperature endurable;
3. Water-proof, moisture-proof, dust-proof, anti-corrosion
4. This is Pallet Wrap Film(LLDPE Stretch Film) produced by three layer common extruding machine, it provide excellent protection for the surface of packed products. It can reduce packaging cost, its economical, labor saving, efficiency increasing. Its easy to use and remove, suitable for palletized packaging of products and transportation operation.
Application:
1. Pallet packaging, carton packaging, wrapping bulk goods, daily necessities packaging;
2. Applied to various fields, such as Electronics, buliding materials, chemicals, materials, automobile components, wire&cable, paper, bottle, can, hardware and electrical materials etc.
Advantage:
Good resistance to stretch strength, resistance to penetrating, ripstop and elongation, especially suitable for the film. Excellent rheological property or melted liquidity, few shearing sensitivity...
1. LLDPE film grade
| Tests | Value | Unit |
| Melt Flow Rate (MFR) | 2.0±0.4 | g/10min |
| Density | 920±2 | Kg/cm3 |
| Tensile Strength at Yield | 8 | Mpa ≥ |
| Tensile Strength at Break | 12 | Mpa ≥ |
| haze | 15 | %≤ |
| Packing | In 25 kg PP woven bags,20MT/20'FCL | |
2. LLDPE for Master Batch Use
| Tests | Value | Unit |
| Melt Flow Rate (MFR) | 20 | g/10min |
| Density | 0.924 | g/cm3 |
| Tensile Strength | MD12 | Mpa |
| TD 10 | ||
| Elongation at Yield | 13 | % |
| Elongation at Break | 200 | |
| Dark Drop Impact | 105 | g |
| Brittle Temperature(F 50) | -70 | °C |
| Vicat Softening Point | 90 | °C |
| Packing | In 25 kg woven bags,20MT/20'FCL | |
3. LLDPE Powder Rotational Molding Grade for Tank Use
| Tests | Value | Unit |
| Melt Flow Rate (MFR) | 3.2 | g/10min |
| Density | 0.939 | g/cm3 |
| Melting Point | 127 | °C |
| Tensile Yield Strength | 21 | Mpa |
| Tensile Strength at Break | 28 | Mpa |
| Elongation at Break | 1,100 | % |
| Flexural Modulus | 750 | Mpa |
| Brittle Temperature | <-60 |
°C |