The lightweight partition wall board uses inorganic binder as the main raw materials, and is made by adding glass fiber grid layout, fire retardants, and other high-performance materials, forming a precision casting ,with superior performance.
1.Green Environmental Protection
The products use natural plant fibers. It has the merits of environmental protection, energy saving, no pollution and no radiation. It can be reduced.
2,Light Texture
About 36kg/-1/9th in weight of the traditional brick wall, the wall can effectively reduce weight .Thus the input of the basis and structure can be reduced.
3.High Strength
Glass-fiber products, using the grid layout enhanced and supported by a variety of high-performance compound modifier, are molded by precision casting at a time. It has the merits of high strength, good toughness and non-deformation.
4.Waterproof
It can be widely used in kitchens, bathrooms and other renovation work.
5.Fire prevention
Added a flame retardant product, it does not produce harmful gases in high temperature. Combustion property is Class A non-combustion .it can be widely used as a firewall.
6.Sound Barrier
The hollow-structured product forms a large number of confined stomatals , with double performances of sound-barrier and sound-absorbing, providing modern society with quiet and comfortable living environment.
7.Temperature Maintenance
After testing, the product performance is better than that of the same thick brick wall or other walls.
8.Easy Installation
It has the following merits: capability of being sawn, shaved, drilled and linked; forming rapidly ; non-deformation while drilling ; good bonded performance with a variety of coatings or cement mortar; hollow-designed products also facilitates the construction of hydropower construction for threading through the installation ,effectively shortening working hours, improving more than double work efficiency.
|
Test item
|
National standard
|
Test result
|
|
Weight(10cm thickness)
|
60Kg/m2
|
35 Kg/m2
|
|
Bending failure load
|
0.75 KM
|
6.5 KM
|
|
Resist impact strength (30kg sand bag)
|
3 times
|
500 times no crack
|
|
Sound insulation
|
40dB
|
43dB
|
|
Max fire resistance
|
A grade 60min
|
188 min
|
|
Single point hanging force
|
≥800N
|
850N no crack by haning 24 hours
|
|
Water resistance
|
7 days
|
No change in water for 8days
|
|
Extremely cold and hot
|
20 times cycles
|
No change by 20 times cycles
|
|
Acid and alkali proof
|
In 5%HCLliquid soaking 24 hours
|
No change by soaking 30 hours
|
|
Water absorption
|
20%
|
18%
|
|
Dry shrinkage
|
≤0.8mm/m
|
0.75mm/m
|
|
Bending
|
≥2000
|
2491
|
|
Thermal conductivity
|
|
0.4816W/M.K
|
|
Freeze-thaw cycle
|
No slip crack
|
26times cycle no slip crack
|
|
Internal radiation index 1Rn
|
≤1.0
|
0.35
|
|
External radiation index 1V
|
≤1.3
|
0.71
|