Specifications
Virgin /Recycled LDPE Raw Material, LDPE Granules, LDPE resin
Low-Density Polyethylene resin
2) Transparent granules
We could supply all kinds of PE resin from the well-known manufacturer. And have been in ths line of business for
If any question, kindly send me a inquiry! The quotation will be send to you within ONE DAY!
1. Basic Information:
Linear low density polyethylene/ LLDPE resin Granules/pellet/LLDPE Virgin or recycled Grade, LLDPE Film Grade, LDPE Granules/LDPE resin/LDPE film Grade/Recycled LDPE, Low-Density Polyethylene resin
2. Grade:
Blown film, Cast film, Healthcare, masterbatch compounding, Pipe extrusion, Rotational moulding, Sheet extrusion, Wire & Cable extrusion
3. Application:
Wire & cable, Geomembranes, Containers & pails, Irrigation, Houseware & appliances Thin wall packaging, Stretch wrap, food wrap, Diaper, Lamination & industrial film, Agricultural & indutrial film, Cast film Stretch film, General purpose film Heavy duty film
4. Data Sheet:
1 LLDPE resin for Packing film:
|
PROPERTY |
UNIT |
SPECIFICATION |
TEST |
|
Melt Flow Index |
g/10min |
≤2.0 |
ASTM D1238 |
|
Density |
g/cm3 |
≤0.945 |
ASTM D1505 |
|
Tensile strength |
Mpa |
≥14.0 |
ASTM D638 |
|
Elongation at break |
% |
≥600 |
ASTM D638 |
|
Brittle temperature at low temperature |
°C |
≤-76 |
ASTM D746 |
|
ESCR ,FO |
H |
≥500 |
ASTM D1693 |
|
Oxidation induction period at 200°C |
Min |
≥30 |
-- |
|
Content of Carbon black |
% |
2.60±0.25 |
-- |
|
Carbon Black dispersion |
-- |
≤3 |
GB2951 |
|
Tensile strength after thermal aging |
Mpa |
≥13 |
GB/T2951.12-2008 |
|
Elongation after thermal aging |
% |
≥500 |
|
|
Dielectric strength |
Mv/m |
≥25 |
ASTM D149 |
|
Volume resistivity |
Ω.m |
≥1*1014 |
ASTM D257 |
|
Dielectric Constant |
-- |
≤2.80 |
ASTM D1505 |
2. Specifications:
|
PROPERTY |
UNIT |
SPECIFICATION |
|
Melt Flow Index |
g/10min |
≤1.0 |
|
Density |
g/cm3 |
≤0.945 |
|
Tensile strength |
Mpa |
≥14.0 |
|
Elongation at break |
% |
≥600 |
|
Brittle temperature at low temperature |
°C |
≤-76 |
|
ESCR ,FO |
H |
≥500 |
|
Carbon Black dispersion |
-- |
-- |
|
Tensile strength after thermal aging |
Mpa |
≥13 |
|
Elongation after thermal aging |
% |
≥500 |
|
Dielectric strength |
Mv/m |
≥25 |
|
Volume resistivity |
Ω.m |
≥1*1014 |
|
change rate of tensile strength after weather aging environment of 0--1008h |
% |
±25 |
|
change rate of elongation after weather aging environment of 0--1008h |
% |
±25 |
|
change rate of tensile strength after weather aging environment of 504--1008h |
% |
±15 |
|
change rate of elongation after weather aging environment of 504--1008h |
% |
±15 |
3. LDPE resin for Blowm film Extrusion: