Click image to view original image
Technology: Acrylic
Chemical type: dimethacrylate ester
Appearance(uncured): Opaque pink paste
Components: One component-require
Viscosity: High
Cure Anaerobic
Application Gasketing and sealing
Strength Medium
CNHYBOND 510 cures when confined in the absence of air between close fittingmetal surfaces, this product is a general gasketing product suitable for hard dispensing or screen printing.
2.Typical Properties of Uncured Material
Specifci gravity@25℃ 1.1
Viscosity ,Brookfield,HBT 25℃,mpa.s(cp):
Spindle TC,speed2.5rpm,helipath: 200,000 to 750,000
3.Instant Sealing Capability
Anaerobic sealants have the ability to resist low on-line test pressures while uncured,this test was performed with uncured product immediately after assembly of an annular polycarbonate sealing surface with an internal diameter of 50 mm and external diameter of 70mm
Pressure Resistance ,Mpa:
Induced Gap 0mm 0.02
Induced Gap 0.125mm 0.01
INDUCED Gap 0.25mm 0.01
4.Typical Performance of Cured Material
Adhesive properties
Cured for 1 hour@22℃
Compressive sherar strength iso 10123
Steel pins and collars(grit N/MM2 >1
Cured for 24 hours@22℃
Compressive shear strength ,iso 10123
Steel pins and collars(grit ,N/MM2 >7.5)
Lap shear strength ,iso4587
Steel(grit blasted) N/MM2 5
Tensile strength , iso 6922
Steel(grit blasted) N/MM2 7.5
5.Directions for Use
A. For best performance bond surfaces should be clean and free from grease
B. The product is designed for close fitting flanged parts with gaps up to 0.25mm
C. Apply manually as a continuous bead or by screen printing to on surface of the flanges
D. Low pressures(<0.05mpa) may be used when testing to confirm a complete seal immediately after assembly and before curing
E. Flanges should be tightened as soon as possible after assembly to avoid shimming
6.Storage
Store in the unopened container in a dry area, and storage instruction are indicated on the label of the
bottle.
Optimal Storage: 2 °C to 8 °C. Storage below 2 °C or greater than 8 °C can adversely affect
product properties. Material removed from containers may be contaminated during using. Do not return
product to the original container. Heng ying Corporation cannot assume responsibility for product which
has been contaminated or stored under conditions other than those previously indicat