HJ260: GB/T17854-1999 F308-H0Cr21Ni10
1.Description:
LH-HJ260 is a faused type low manganese-oxide flux with vitreous granule of gray color about 10-60 mesh in size. It is suitable for use DECP. The arc is table and the bead appearance is good.
2.Usage:
In combination with stainless steel wires (such as H0Cr21Ni10,H0Cr21Ni10Ti,H3Cr13 ect.), this flux is suitable for weldingof appopriate acid resistance stainless steel structures, and is also suitable for surfacing of rolls.
3.GUIDELINES FOR USAGE:
1.Dry the flux at 300-400ºC for 2 hours before use.
2.Completely remove rust, oil and dirt from the groove surface prior to welding.
4.Chemical Composition(%)
| MnO+SiO2 | CaF2+CaO+MgO | Al2O3 | S | P |
| 31-38 | 39-50 | ≥19 | ≤0.06 | ≤0.08 |
5.Our Factory Introduction
LAIWU HULING WELDING is one of leading biggest manufacturer of Submerged ARC welding flux in China. The annual capacity of production is growing and up to12000 metric tons of agglomerated flux and 5000 metric tons of fused flux. The factory has established the R&D laboratory with the advanced inspection equipments in field of welding materials. Our company is located at Laiwu City near by the Jinan International Airport, and also is near the TAISHAN Mount of Shandong Province, China.
The Submerged-ARC welding flux has been approved and passed the inspection of quality with the province grade and the national grade in China. We strictly executed and produced the welding flux according to the industrial standards of GB/T 5293-1999, GB/T 12740-2003, GB/T17854-1999 and the China Classification Society-1996 completely. Our quality management has passed IS09001-2008 Quality System Certification.
The welding flux has been widely used in the Chemical engineering equipment, Heavy machinery, Pressure vessel, Boiler, Gas cylinder body, Spiral welded steel pipe, Steel structure building H-beam steel etc. We have been exported the welding flux to India, Indonesia, Egypt, Japan, Philippine and Jordan. The foreign customer usually purchased and preferred to the high quality Agglomerated flux ( LH-SJ101;LH-SJ301;LH-SJ501;LH-HF101G ) and Manganese oxide fused flux.